SEC is an industry leader when it comes to Passivation site assessments, estimates, project planning and execution. We offer full turn-key Passivation services. Contact us via Phone 803 789 7241 or Email michaelreed@truvista.net
WHAT IS STAINLESS STEEL PASSIVATION?
Stainless passivation is the process by which stainless steel will spontaneously form a chemically inactive surface when exposed to air or other oxygen-containing environments. Some important facts to know when considering passivating stainless steel:
-
Steels containing more than 11% Chromium are capable of forming an invisible, inert or passive, self-repairing oxide film on their surface. It is this passive layer that gives stainless steels their corrosion resistance.
-
If a stainless steel surface is scratched, then more Chromium is exposed which reacts with oxygen allowing the passive layer to reform. However, if a particle of carbon steel is embedded in the scratch then the passive layer cannot reform and corrosion will occur when the metal is wetted or exposed to a corrosive environment.
-
Stainless passivation is the chemical treatment of a stainless steel surface with a mild oxidant such as citric acid passivation solution. This process is to accelerate the process noted above in No. 1.
-
Passivating stainless steel is the removal of exogenous iron or iron compounds from the surface by means of a chemical dissolution, most typically by a treatment with an citric acid passivation solution that will remove the surface contamination but will not significantly affect the stainless steel itself.
-
Passivation also is accomplished by stainless steel electropolishing. Electropolishing is an electrochemical process that is a super passivator of stainless steel and results in a more passive surface than the other methods mentioned above.
This last step is necessary because during handling and processing such as rolling, forming, machining, pressing, tumbling, and lapping, particles of iron or tool steel or abrasive particles may be embedded in or smeared on or into the surfaces of stainless steel components. If allowed to remain, these particles may corrode and produce rust spots on the stainless steel. This is due to the formation of a galvanic couple between two dissimilar metals that can promote a corrosive reaction. To dissolve the embedded or smeared iron and prevent this condition, as well as restore the original corrosion-resistant surface, semi-finished or finished parts are given a 'passivation' treatment.